利用计算机实现自动、准确的秀丽隐杆线虫(C.elegans)的各项形态学参数分析,至关重要的是从显微图像上分割出线虫体态,但由于显微镜下的图像噪声较多,线虫边缘像素与周围环境相似,而且线虫的体态具有鞭毛和其他附着物需要分离,多方面因素导致设计一个鲁棒性的C.elegans分割算法仍然面临着挑战。针对这些问题,提出了一种基于深度学习的线虫分割方法,通过训练掩模区域卷积神经网络(Mask R-CNN)学习线虫形态特征实现自动分割。首先,通过改进多级特征池化将高级语义特征与低级边缘特征融合,结合大幅度软最大损失(LMSL)损失算法改进损失计算;然后,改进非极大值抑制;最后,引入全连接融合分支等方法对分割结果进行进一步优化。实验结果表明,相比原始的Mask R-CNN,该方法平均精确率(AP)提升了4.3个百分点,平均交并比(mIOU)提升了4个百分点。表明所提出的深度学习分割方法能够有效提高分割准确率,在显微图像中更加精确地分割出线虫体。     

多先验融合的图像显著性目标检测算法

为了更加准确地检测出图像中的显著性目标，提出了多先验融合的显著性目标检测算法。针对传统中心先验对偏离图像中心的显著性目标会出现检测失效的情况，提出在多颜色空间下求显著性目标的最小凸包交集来确定目标的大致位置，以凸包区域中心计算中心先验。同时通过融合策略将凸包区域中心先验、颜色对比先验和背景先验融合并集成到特征矩阵中。最后通过低秩矩阵恢复模型生成结果显著图。在公开数据集MSRA1000和ESSCD上的仿真实验结果表明，MPLRR能够得到清晰高亮的显著性目标视觉效果图，同时F，AUC，MAE等评价指标也比现有的许多方法有明显提升。     

Relationships between the accumulative damage and dielectric properties of woven BN-coated Hi-Nicalon™ SiC fibre-reinforced SiC matrix composites

The accumulative damage behaviour of BN-coated Hi-Nicalon™ SiC fibre-reinforced SiC matrix composite was examined under tensile cyclic loading at room and elevated temperatures. The accumulative damage occurring during the cyclic loading was quantitatively characterised using the damage parameter obtained by the hysteresis loop curves. The damage parameter increased with increasing applied stress beyond the matrix cracking stress, and it subsequently retained a nearly constant value until just before fracture. Moreover, the dielectric constant, dielectric loss and loss tangent of the composite were measured before and after the fracture in the frequency range 1–1000 MHz. The dielectric properties had similar frequency dependency before and after the fracture. However, the dielectric constant, dielectric loss and loss tangent were lower in the post-fractured specimens than in the pristine ones. The reduction of the dielectric properties was associated with the accumulative damage stored in the specimens. In addition, the relationships between the dielectric properties and the damage parameter were described in detail.     

Monomer casting nylon-6-b-polyether amine copolymers: Synthesis and properties

MC nylon-6-b-polyether amine copolymers were prepared with macro-initiator based on amino-terminated polyether amine functionalized with isocyanate via in-situ polymerization. It was found that the introduction of polyether amine delayed the polymerization process of caprolactam by increasing apparent activation energy and pre-exponential factor, resulting in the decrease of molecular weight of nylon-6. The motion of molecular chain of the copolymers was easy because of the decreased hydrogen bonds and weakened inter-molecular forces. The physical entanglement of molecular chains of the copolymers was significant and strong which increased the entanglement density. Only the nylon-6 phase crystallized in the copolymers and the crystal grain size, spherulite size and crystallinity of the copolymers decreased. A small amount of γ crystal formed at high polyether amine content. The copolymers presented obvious strain hardening behavior in stress-strain curves and the loss factor dramatically increased while the glass transition temperature and storage module decreased. The fracture surface of the copolymers became rough and presented hairy structure, indicating that the toughening mechanism of the copolymers corresponded to the multi-layer crack extension mechanism.     

Controlling Au electrode patterns for simultaneously monitoring electrical actuation and shape recovery in shape memory polymer

This paper presents an effective approach to achieve efficient electrical actuation and monitoring of shape recovery based on patterned Au electrodes on shape memory polymer (SMP). The electrically responsive shape recovery behavior was characterized and monitored by the evolution change in electrical resistance of patterned Au electrode. Both electrical actuation and temperature distribution in the SMP have been improved by optimizing the Au electrode patterns. The electrically actuated shape recovery behavior and temperature evolution during the actuation were monitored and characterized. The resistance changes could be used to detect beginning/finishing points of the shape recovery. Therefore, the Au electrode not only significantly enhances the electrical actuation performance to achieve a fast electrical actuation, but also enables the resistance signal to detect the free recovery process.     

Mechanical properties of a self-healing fibre reinforced epoxy composites

Inspired by biological systems in which damage triggers an autonomic healing response, a polymer composite material that can heal itself when cracked has been developed. In this work, compression and tensile properties of a self-healed fibre reinforced epoxy composites were investigated. Microencapsulated epoxy and mercaptan healing agents were incorporated into a glass fibre reinforced epoxy matrix to produce a polymer composite capable of self-healing. The self-repair microcapsules in the epoxy resin would break as a result of microcrack expansion in the matrix, and letting out the strong repair agent to recover the mechanical strength with a relative healing efficiency of up to 140% which is a ratio of healed property value to initial property value or healing efficiency up to 119% if using the healed strength with the damaged strength.     

Accounting for the uncertainties in the estimation of average shear wave velocity using V S– N correlations

Site-specific seismic hazard analysis is crucial for designing earthquake resistance structures, particularly in seismically active regions. Shear wave velocity ( V _S) is a key parameter in such analysis, although the economy and other factors restrict its direct field measurement in many cases. Various V _S–SPT– N correlations are routinely incorporated in seismic hazard analysis to estimate the value of V _S. However, many uncertainties question the reliability of these estimated V _S values. This paper comes up with a statistical approach to take care of such uncertainties involved in V _S calculations. The measured SPT– N values from all the critical boreholes were converted into statistical parameters and passed through various correlations to estimate V _S at different depths. The effect of different soil layers in the boreholes on the Vs estimation was also taken into account. Further, the average shear wave velocity of the top 30 m soil cover ( V _S30) is estimated after accounting for various epistemic and aleatoric uncertainties. The scattering nature of the V _S values estimated using different V _S– N correlations was reduced significantly with the application of the methodology. Study results further clearly demonstrated the potential of the approach to eliminate various uncertainties involved in the estimation of V _S30 using general and soil-specific correlations.     

刮板输送机中板仿生耐磨优化试验研究

刮板输送机中板磨损失效已成为输送机运行故障的主要原因之一，为了提高中板耐磨性，基于蜣螂非光滑单元进行了仿生中板设计，以磨损量为响应值，进行了单因素和响应面法优化试验。根据响应面法试验结果得到的因素显著性影响顺序（从高至低）依次为：径向距离，深径比，直径，节距角。基于试验结果建立了磨损量与因素的回归预测模型，经试验对比发现，预测模型与真实试验的相对误差为3.2%。在特定工况（煤散料粒度为6~8 mm、载荷为20 N、刮板链速为0.65 m/s及试验时长为6 600 s）下，当深径比为1.41、直径为0.69 mm、节距角为6.55°和径向距离为4.66 mm时，磨损量最小，仿生中板的耐磨性提高了12.6%。分析其耐磨机理发现，与光滑板相比，仿生板的磨粒磨损及黏着磨损较轻。凹坑分布可破坏持续切削中板表面的煤粒运动状态。中板的仿生优化可为今后刮板输送机的设计提供一定参考。     

Investigations on grinding process of woven ceramic matrix composite based on reinforced fiber orientations

Fiber orientations play the decisive role in grinding process of woven ceramic matrix composites, but the influence of woven fibers in grinding process is not clear. This paper studies the surface quality and grinding force by comparing different woven surfaces. Through a series of experiments in optimized sampling conditions, we analyze characteristics of the material surface topography height, wave distribution and surface support properties in details. And we find some outstanding characteristics of the surface microstructure. We also study the influence of grinding processing parameters on surface microstructure. The results show that machining surface which contains more parallel fibers is rougher and more keenness than gauss surface. Grinding wheel speed and depth of cut have great influence on surface topography and surface support properties. And it is discovered that grinding forces are also highly dependent on fiber orientations. The mechanism of the grinding phenomena is also analyzed in this paper according to knowledge of fracture mechanics and mechanical damage phenomenology. The research obtained will be an important technical support on improving the processing quality of woven ceramic matrix composites.